Keluli tahan haba tuangan EN10295
Syarikat kami menghasilkan keluli tahan haba selaras dengan piawaian Eropah, menyediakan penyesuaian pemprosesan, dialu-alukan untuk membeli
Sifat mekanikal disuhu bilik
|
Jawatan |
Haba rawatan |
Tegangan ujian |
Kekerasan HB maks. |
||||||
|
Simbol |
Suhu ijazah |
Fpo,2 MPa a min. |
Rm MPa a min. |
A % min. |
|||||
|
Nama |
Nombor |
||||||||
|
Feritik dan austenit - gred ferit |
GX30CrSiz b |
1.4710 |
+AC |
800 hingga 850 |
300 |
||||
|
GX40CrSi13 |
1.4729 |
+AC |
800 hingga 850 |
300 |
|||||
|
GX40CrSi17 |
1.4740 |
+AC |
800 hingga 850 |
300 |
|||||
|
GX40CrSi24 |
1.4745 |
Tidak haba rawatan |
d |
||||||
|
GX40CrSi28 |
1.4776 |
d |
|||||||
|
GX130CrSi29 |
1.4777 |
d |
|||||||
|
GX160CrSi18 |
1.4743 |
d |
|||||||
|
GX40CrNiSi27-4 |
1.4823 |
250 |
550 |
3 |
d |
||||
|
Gred Austenit |
GX25CrNiSi18-9 |
1.4825 |
230 |
450 |
15 |
||||
|
GX40CrNiSi22-10 |
1.4826 |
230 |
450 |
8 |
|||||
|
GX25CrNiSi20-14 |
1.4832 |
230 |
450 |
10 |
|||||
|
GX40CrNiSi25-12 |
1.4837 |
220 |
450 |
6 |
|||||
|
GX40CrNiSi25-20 |
1.4848 |
220 |
450 |
8 |
|||||
|
GX40CrNiSiNb24-24 |
1.4855 |
220 |
450 |
4 |
|||||
|
GX35NiCrSi25-21 |
1.4805 |
220 |
430 |
8 |
|||||
|
GX40NiCrSi35-17 |
1.4806 |
220 |
420 |
6 |
|||||
|
GX40NiCrSiNb35-18 |
1.4807 |
220 |
420 |
4 |
|||||
|
GX40NiCrSi38-19 |
1.4865 |
220 |
420 |
6 |
|||||
|
GX40NiCrSiNb38-19 |
1.4849 |
220 |
420 |
4 |
|||||
|
GX10NiCrSiNb32-20 |
1.4859 |
180 |
440 |
20 |
|||||
|
GX40NiCrSi35-26 |
1.4857 |
220 |
440 |
6 |
|||||
|
GX40NiCrSiNb35-26 |
1.4852 |
220 |
440 |
4 |
|||||
|
GX50NiCrCo20-20-20 |
1.4874 |
320 |
420 |
6 |
|||||
|
GX50NiCrCoW35-25- 15-5 |
1.4869 |
270 |
480 |
5 |
|||||
|
GX40NiCrNb45-35 |
1.4889 |
240 |
440 |
3 |
|||||
|
Nikel dan kobalt |
aloi asas |
G-NiCr28W |
2.4879 |
240 |
440 |
3 |
|||
|
G -CoCr28 |
2.4778 |
235 |
490 |
6 |
|||||
|
G-NiCr50Nb |
2.4680 |
230 |
540 |
8 |
|||||
|
G-NiCr15 |
2.4815 |
200 |
400 |
3 |
|||||
|
1MPa=1 N/mm2 b Jika gred ini digunakan untuk tuangan tahan haus, maka ia boleh dihantar tanpa rawatan haba. c +A bermaksud:Penyepuhlindapan d Tuangan boleh juga dibekalkan dalam keadaan sepuhlindap dalam kes ini nilai kekerasan maksimum boleh dipersetujui. |
|||||||||